STARFLEX CAR PARK - CEMENT
• Substrate to be treated must be free from debris and dust. Clean the substrate by either water jetting or air blowing and/or brushing.
PRIMING:
• DUROGLASS FU RAPID, water based rapid 2 component modified epoxy DPM primer designed for gaining adhesion on humid substrate up to 10 bar of back-pressure.
Solves humidity problems allowing safe application for all kinds of floorings. Rapid curing allowing overcoating within hours even in cold temperatures 4 hours, 6° C, 75% RH.
Can be used for scratch coats or roller applications. Low VOC.
Consumption rate is 0,300-500 kg/m² per coat making sure that areas with greater absorption rate should be treated again.
WATERPROOFING MEMBRANE:
• STARFLEX HR is rapid curing pure polyurea two-component 100% solids elastomeric, fast hardening with a very fast attainment of the final mechanical characteristics. It can be applied also in vertical and ceil-ing, Wide range application with ability to spray at very low tempera-tures and/or high humidity.
The product can be applied exclusively by spraying devices (propor-tional hot spray) with two-component airless pumping units, equipped with a mixing gun.
The necessary equipment must also include pre-heating the separate components at temperatures of at least 65-75 ° C. The best results are obtained with pressures of at least 190 – 210 Bar, material tempera-tures of 75 ° C with heated feeding pipes for the spray gun.
TOP COAT:
• POLISTAR E/P, two component elastic polyurethane based UV- resistant, anti-skid and wear resistant protective coating, one component elastic aliphatic polyurea based top coat for manual application at a rate of 0,15-0,25 kg/m² per coat.
The product for anti-slip can be added /charged with 0,1-0,3 mm quartz and or be broadcasted with 0,1- 0,5 quartz on the first of the 2 top coats.
When 2 coats must be applied do not let more than 48 hours between the coats.
• POLISTAR E/2, 2k polyurethane based uv- resistant, anti-skid and wear resistant protective coating, with a consumption of 0,150 Kg/m2.
• The over coating has to be applied within 3-4 hours maximum after the appli-cation of STARFLEX HR.
• High elasticity, tenacity, resistance to puncturing, abrasion resistance and wear resistance with the ability of crack-bridging.
• Water impermeabile, excellent chemical resistance and corrosion resistance.
• Substrate application temperature range: from -20°C a +40°C.
• Operating temperatures: -30°C – +100°C.